Question: When we do cardonitriding or casehardening operation for a plain carbon steel the case depth, hardness & microstructure are not alike why and what are the basic thing, which makes such a difference.

Answer: Usually that will depend on the time and temperature, as well as chemical composition of the furnace atmosphere you are using.

If these variables are not kept well controlled, they may cause very different results. Please note that time and temperature are correlated, the more temperature, the less time and lesser diffusion control.

Usually that will depend on the time and temperature, as well as chemical composition of the furnace atmosphere you are using.

If these variables are not kept well controlled, they may cause very different results. Please note that time and temperature are correlated, the more temperature, the less time and lesser diffusion control. Source: CoolInterview.com

If you have the better answer, then send it to us. We will display your answer after the approval.

Rules to Post Answers in CoolInterview.com:-

• There should not be any Spelling Mistakes.
• There should not be any Gramatical Errors.
• Answers must not contain any bad words.
• Answers should not be the repeat of same answer, already approved.
• Answer should be complete in itself.

Name :*
Email Id :*
Answer :*
Verification Code	Not readable? Load New Code
Enter the above shown code: *
	Inform me about updated answers to this question